AeroST carbon non-crimp fabric UMS 20 g/m²
Fibre: Tenax® UMS40 24k / 800 tex
HM carbon fibres (high modulus = high modulus fibres) are suitable for stiffness-
relevant applications. Compared to standard types such as Tenax® HTS40, this fibre
offers more than 60% increased stiffness combined with higher tensile strength and
good elongation at break.
Width: 60 cm
Length: 310 cm
Areal weight: 20 g/m²
If very thin components are manufactured, warping can occur if a non-mirrored lay-
up is used. For this reason, we only offer sets with 2 different variants (+/- 45° and -/
+ 45°).
In this biaxial NCF, two unidirectional layers are bonded at an angle of ± 45° with a
neutral binder. Drapeability (flexibility) is significantly improved compared to
conventional NCF with sewing thread or thermoplastic Scrim. Due to the very low
degree of thread deflection, the properties of the fibres are utilized to the full.
Compared to filament fabrics, this allows the production of a parts surface without
visible fibre print-through, which is still as stable even after months.